| 特性級(jí)別 | 阻燃級(jí)|||增韌級(jí)||| |
| 牌號(hào) | INP362 |
| 加工級(jí)別 | 注墮級(jí)||| |
| 品名 | sabic ABS INP362 |
| 廠家(產(chǎn)地) | 美國sabic |
| 用途級(jí)別 | 填充級(jí)|||電動(dòng)工具配件||| |
丙烯腈丁二烯苯乙烯
SABIC Innovative Plastics
產(chǎn)品說明
SABIC INP108 is a high rubber ABS impact modifier resin, and is based on polybutadiene rubber. Offers superior impact efficiency, especially at low temperatures. Reduces notch sensitivity when alloyed with engineering polymers. Disperses easily. Provides abrasion and chemical resistance to polymers.
附加服務(wù)
耐低溫沖擊ABS INP362 ABS
| 基本信息 | |
|---|---|
| 特性 |
|
| 用途 |
|
| 添加劑 |
|
| 表面電阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 體積電阻率 | > 1.0E+15 | ohms·cm | IEC 60093 |
| 介電強(qiáng)度 | IEC 60243-1 | ||
0.800 mm, 在油中 | 35 | kV/mm | |
1.60 mm, 在油中 | 26 | kV/mm | |
3.20 mm, 在油中 | 18 | kV/mm | |
| 相對(duì)電容率 | IEC 60250 | ||
50 Hz | 2.70 | ||
60 Hz | 2.70 | ||
1 MHz | 2.60 | ||
| 耗散因數(shù) | IEC 60250 | ||
50 Hz | 4.0E-3 | ||
60 Hz | 4.0E-3 | ||
1 MHz | 9.0E-3 | ||
| 漏電起痕指數(shù) | 600 | V | IEC 60112 |
| 可燃性 | 額定值 | 單位制 | 測(cè)試方法 |
|---|---|---|---|
| UL 阻燃等級(jí)(1.50 mm, Testing by SABIC) | HB | UL 94 | |
| 灼熱絲易燃指數(shù)(1.00 mm) | 650 | °C | IEC 60695-2-12 |
耐低溫沖擊ABS INP362 ABS
| 物理性能 | 額定值 | 單位制 | 測(cè)試方法 |
|---|---|---|---|
| 比重 | |||
-- | 0.998 | g/cm3 | ASTM D792 |
-- 1 | 1.01 | g/cm3 | ISO 1183 |
| 表觀密度 | 0.35 | g/cm3 | ASTM D1895 |
| Mean Particle Size | 400.0 | μm | 內(nèi)部方法 |
| Rubber Content | 32 | % | 內(nèi)部方法 |
| Total NA Volatiles | 0.10 | % | 內(nèi)部方法 |
| 硬度 | 額定值 | 單位制 | 測(cè)試方法 |
| 肖氏硬度(邵氏 D) | 58 | ISO 868 |
| 注射 | 額定值 | 單位制 | |
|---|---|---|---|
| 干燥溫度 | 85.0 到 95.0 | °C | |
| 干燥時(shí)間 | 2.0 到 4.0 | hr | |
| 建議的*水分含量 | 0.10 | % | |
| 料斗溫度 | 60.0 到 80.0 | °C | |
| 料筒后部溫度 | 200 到 240 | °C | |
| 料筒中部溫度 | 220 到 260 | °C | |
| 料筒前部溫度 | 220 到 260 | °C | |
| 射嘴溫度 | 210 到 250 | °C | |
| 加工（熔體）溫度 | 220 到 260 | °C | |
| 模具溫度 | 40.0 到 80.0 | °C |
耐低溫沖擊ABS INP362 ABS